Adhesive 88-NP-43

Adhesive 78 BCSP-M is a modification of adhesive 78 BCSP, belonging to cold-curing adhesives based on chloroprene rubber, intended for bonding rubber (including sponge rubber) with metal, wood, glass and other surfaces. They provide strong joints resistant to fresh and sea water and operate over a wide temperature range.

Category: Rubber Adhesives

Purpose: Aerospace industry

Purpose: Shipbuilding

Purpose: Automotive industry

Purpose: Construction and industry

Technical specifications

Main purpose and application

Technical specifications

1. Appearance: From yellow-green to dark beige 2. Homogeneity: Homogeneous 3. Conditional viscosity (ball viscometer), s: 10–40 4. Bond strength of vulcanized rubber P-56 (TU 38 0051166-98) with D-16 aluminum alloy (GOST 21631) or St.3 steel (GOST 380, GOST 21488) at (23±5)°C after 24 h curing: – Peel strength, N/mm (kgf/cm), min: 2.26 (2.3) – Tensile strength, MPa (kgf/cm²), min: 1.08 (11.0) After 48 h curing: – Peel strength, N/mm (kgf/cm), min: 2.46 (2.5) – Tensile strength, MPa (kgf/cm²), min: 1.28 (13.0)

Main purpose and application

Products bonded with 88-NP-43 adhesives are intended for operation in air at temperatures from -40°C to +90°C.
Bonding with these adhesives is resistant to fresh and seawater in normal conditions.

Application areas:

Automotive industry: Bonding rubber seals, sound insulation, interior trim.
Shipbuilding: Installation of rubber products resistant to seawater.
Construction: Bonding rubber with concrete, wood, metal structures.
Industry: Production of furniture (foam bonding), footwear, aviation components.
Universal applications: Rubber, leather, glass, ceramics, textiles in any combinations.